Product Info for UNITHANE IC-900

Unithane IC-900 is a NMP containing, soft, low VOC, high gloss, APEO free, waterbased polyurethane dispersion; with very good adhesion, flexibility and automotive grade properties. Suitable for use in a formulated primer coat for concrete, graphic arts, textiles and selected plastics.

Industrial Applications:

This product is recommended for: Automotive Interiors - Non-Leather, Paint and Coating Resins, Graphic Arts, Flexible Substrates, Adhesives

Product Characteristics:

Product Class	Solids %	pH	Viscosity @25ºC	Gloss	VOC g/L	Tensile (D-882)	Elongation (%)	Modulus 100% (psi)	Sward Hardness
	34 - 36	7.5 - 8.5	150 cps	80	49.48	3800 psi	1000%	570 psi	6

Full product details can be found in this section:

GENERAL INFORMATION

Special Features: NMP Containing, Low VOC (<100 g/L) Application Types - Industrial Coatings: Interior, Exterior, Automotive, Aircraft, Synthetic Leather, Concrete, Paint, Metal, Graphic Arts, OPV, Paper, Textiles, Plastics - Flexible, Plastics - Rigid, Adhesive/Primer, Heatseal, Blister Pack

TYPICAL SPECIFICATIONS

Total Solids %: 34 - 36 pH: 7.5 - 8.5 Viscosity @ 25⁰ C: 150 cps VOC (Grams/Liter): 49.48 VOC (% of total weight): 4.94 Specific Gravity: 1.03 Appearance: Semi-translucent Gloss (60): 80 Shelf Life: 18 months Harmonize Tariff Number: 3909.50.5000

TYPICAL FILM PROPERTIES

Film Appearance after Curing: Clear Tensile (D-882): 3800 psi Tensile at 100% Elongation: 570 psi Elongation (D-882): 1000% Cold Crank (ISO 17233): <-30C Softening Point: 130C Pencil Hardness (D-3363): <6B Sward Hardness (D-2134): 6 UV Resistance (D-4587): No Damage (1000 hours at 340 nm) Impact Resistance (D-2794): No Damage at 160 psi (Direct or Reverse) Tabor Abrasion (D-4060): 12 mg loss (CS-10, 1000g 1000 cycles) Mandrel Bend (D-522): Pass 1/8, 1/4, 3/8, 1/2, 5/8, 3/4, 1 Dry Time (D-5895): 70 minutes Hydrolysis Resistance (200 hours, 70ºC, 95% RH): Retained 70% of Tensile Properties

CHEMICAL RESISTANCE TESTING (D-1308)

note: 5= no damage, films dried for 15 minutes at 80ºC, then equalized at room temp for 7 days. Water: 5 Acetic Acid: 3 Ammonia: 2 Methyl Ethyl Ketone: 1 2-Propanol: 1 Toluene: 4 Gasoline: 5

VARIOUS SUBSTRATE CROSS CUT ADHESION (D-3359)

Cold Roll Steel - Unpolished: 5B Aluminum - Untreated: 5B Brass - Untreated: 5B ABS - Untreated: 5B Polycarbonate - Untreated: 5B Nylon - Untreated: 5B HDPE - Untreated: 0B
Certified to ISO-9001: 2008
Contact Information:

3 Malcolm Hoyt Drive
Newburyport, Massachusetts 01950 ∙ U.S.A.
Tel: (978) 465-1717 ∙ Fax: (978) 465-4194
E-mail: union@unionspecialtiesinc.com ∙ www.unionspecialtiesinc.com

Disclaimer:

The information and data contained herein are believed to be correct. However, we do not warrant either expressly or by implication the accuracy thereof.