UNITHANE IC-151 NF is an anionic APEO free dispersion of an aliphatic polyester-based urethane in water. UNITHANE IC-151 NF is designed for industrial coating applications requiring good gloss, chemical resistance and adhesion to a variety of substrates.

Application:

UNITHANE IC-151 NF polyurethane dispersion can be compounded for a number of industrial coating applications: including clear, hard coatings for plastics, untreated aluminum, treated steel and concrete floor coatings.

The performance of UNITHANE IC-151 NF can be further enhanced by blending with other Union polyurethane dispersions or by the use of external crosslinking like: polyfunctional aziridines, water dispersible isocyanates or polyfunctional carbodiimides.

Industrial Applications:

This product is recommended for: Paint and Coating Resins

Product Characteristics:

Product Class	Solids %	pH	Viscosity @25ºC	Gloss	VOC g/L	Tensile (D-882)	Elongation (%)	Modulus 100% (psi)	Sward Hardness
	31 – 33	8.0 – 10.0	10-150 cps.	80-100	102-104	3000 psi	50%	n/a	32

Full product details can be found in this section:

GENERAL INFORMATION

Special Features: NMP-Free (NF)
Application Types – Industrial Coatings: Interior, Exterior, Flooring, Wood, Concrete, Paint, Metal, Graphic Arts, OPV, Paper, Plastics – Rigid

TYPICAL SPECIFICATIONS

Total Solids %: 31 – 33
pH: 8.0 – 10.0
Viscosity @ 25⁰ C: 10-150 cps.
VOC (Grams/Liter): 102-104
VOC (% of total weight): 9.0-11.0
Specific Gravity: 1.03-1.06
Appearance: Semi-translucent
Gloss (60): 80-100
Freeze/Thaw Cycles (D-2243): 3+ cycles
Shelf Life: Maximum 12 months
Harmonize Tariff Number: 3909.50.6000

TYPICAL FILM PROPERTIES

Film Appearance after Curing: Clear
Tensile (D-882): 3000 psi
Tensile at 100% Elongation: n/a
Elongation (D-882): 50%
Cold Crank (ISO 17233): 5°C
Softening Point: 175°C
Pencil Hardness (D-3363): 4B
Sward Hardness (D-2134): 32
UV Resistance (D-4587): No Damage (1000 hours at 340 nm)
Impact Resistance (D-2794): Damage at 160 psi (Direct or Reverse)
Tabor Abrasion (D-4060): 20 mg loss (CS-10, 1000 cycles)
Mandrel Bend (D-522): Cracked @ 1/8
Dry Time (D-5895): 30 minutes
Hydrolysis Resistance (200 hours, 70ºC, 95% RH): Retained 90% of Tensile Properties

CHEMICAL RESISTANCE TESTING (D-1308)

note: 5= no damage, films dried for 15 minutes at 80ºC, then equalized at room temp for 7 days.
Water: 5
Acetic Acid: 5
Ammonia: 5
Methyl Ethyl Ketone: 5
2-Propanol: 5
Toluene: 5
Gasoline: 5

VARIOUS SUBSTRATE CROSS CUT ADHESION (D-3359)

Cold Roll Steel – Unpolished: 5B
Aluminum – Untreated: 5B
Brass – Untreated: 5B
ABS – Untreated: 5B
Polycarbonate – Untreated: 5B
Nylon – Untreated: 5B
HDPE – Untreated: 0B

Certified to ISO-9001:2015

Contact Information:

3 Malcolm Hoyt Drive
Newburyport, Massachusetts 01950 ∙ U.S.A.
Tel: (978) 465-1717 ∙ Fax: (978) 465-4194
E-mail: union@unionspecialtiesinc.com ∙ www.unionspecialtiesinc.com

Disclaimer:

The information and data contained herein are believed to be correct. However, we do not warrant either expressly or by implication the accuracy thereof.

[Please note that due to the Chinese Trademark Office opposition decision, products destined for the China marketplace in the category of “Adhesives for Industrial purposes: Polyurethane,” will NOT contain the trade name “UNITHANE” but will be labeled only with the letter or number designation. Please contact us if there are any questions. Thank you.]