Unithane IC-910 NF is a NMP free, soft, low VOC, high gloss, APEO free, waterbased polyurethane dispersion; with exceptional adhesion, flexibility and automotive grade properties.

Specifically designed for use in a formulated primer coat for concrete, graphic arts, textiles and selected plastics.

Industrial Applications:

This product is recommended for: Automotive Interiors – Non-Leather, Paint and Coating Resins, Graphic Arts, Flexible Substrates, Adhesives

Product Characteristics:

Product Class Solids % pH Viscosity @25ºC Gloss VOC g/L Tensile (D-882) Elongation (%) Modulus 100% (psi) Sward Hardness
31 – 33 7.0 – 8.0 10-500 cps 80 – 100 55-65 3850 psi 1000% 600 psi 2

Full product details can be found in this section:

GENERAL INFORMATION

Special Features: NMP-Free (NF), Low VOC (<100 g/L)
Application Types – Industrial Coatings: Interior, Exterior, Automotive, Aircraft, Synthetic Leather, Concrete, Paint, Metal, Graphic Arts, OPV, Paper, Textiles, Plastics – Flexible, Plastics – Rigid, Adhesive/Primer, Heatseal, Blister Pack

TYPICAL SPECIFICATIONS

Total Solids %: 31 – 33
pH: 7.0 – 8.0
Viscosity @ 25⁰ C: 10-500 cps
VOC (Grams/Liter): 55-65
VOC (% of total weight): 5.5-6.5
Specific Gravity: 1.01-1.04
Appearance: Semi-translucent
Gloss (60): 80 – 100
Freeze/Thaw Cycles (D-2243): 0
Shelf Life: Maximum 12 months
Harmonize Tariff Number: 3909.50.6000

TYPICAL FILM PROPERTIES

Film Appearance after Curing: Clear
Tensile (D-882): 3850 psi
Tensile at 100% Elongation: 600 psi
Elongation (D-882): 1000%
Cold Crank (ISO 17233): below -30°C
Softening Point: 130°C
Pencil Hardness (D-3363): <6B
Sward Hardness (D-2134): 2
UV Resistance (D-4587): No Damage (1000 hours at 340 nm)
Impact Resistance (D-2794): No Damage at 160 psi (Direct or Reverse)
Tabor Abrasion (D-4060): 13 mg loss (CS-10, 1000g 1000 cycles)
Mandrel Bend (D-522): Pass 1/8, 1/4, 3/8, 1/2, 5/8, 3/4, 1
Dry Time (D-5895): 35 minutes
Hydrolysis Resistance (200 hours, 70ºC, 95% RH): Retained 70% of Tensile Properties

CHEMICAL RESISTANCE TESTING (D-1308)

note: 5= no damage, films dried for 15 minutes at 80ºC, then equalized at room temp for 7 days.
Water: 5
Acetic Acid: 3
Ammonia: 2
Methyl Ethyl Ketone: 1
2-Propanol: 2
Toluene: 4
Gasoline: 5

VARIOUS SUBSTRATE CROSS CUT ADHESION (D-3359)

Cold Roll Steel – Unpolished: 5B
Aluminum – Untreated: 5B
Brass – Untreated: 5B
ABS – Untreated: 5B
Polycarbonate – Untreated: 5B
Nylon – Untreated: 5B
HDPE – Untreated: 0B